PA12 WITCOM 2010/039

Use performance

1, a typical range of applications: water table and other business equipment, cable sets, mechanical cam, slide mechanism and bearings.
2, Injection molding conditions: a) drying: moisture content must be less than 0.1% prior to processing. If the material is exposed to the air storage, it is recommended to 85C in hot air dried for 4 to 5 hours. If the material is stored in a sealed container, then after 3 hours Temperature balance can be used directly. b) melting temperature: 240 300C; ordinary characteristics of materials should not exceed 310C have flame-retardant characteristics of the material do not exceed 270C. c) Mold temperature: For the unreinforced material is 30 ~ 40C, the thin wall or large area element 80 to 90c and 90 to 100C, for reinforced. The increase in temperature will increase the degree of crystallinity of the material. PA12 it is very important to accurately control the mold temperature. d) Injection pressure: the maximum to 1000bar (recommend using low pressure and high melting temperature). e) injection speed: high-speed (for a material with glass additives is better).
Runners and gates: for not additive materials, due to low viscosity materials, the diameter of the flow channel should be about 30mm. For enhanced material requires 5 ~ 8mm diameter of the crowd Road. The shape of the flow channel should all circular. The injection port should be as short as possible. You can use various forms of gates. Large plastic parts do not use small gate, which is in order to avoid the plastic parts are too high a pressure or too large shrinkage. The best gate thickness equal to the thickness of the plastic parts. If using submarine gates, it is recommended that the minimum diameter of 0.8mm. Hot runner mold is very effective, but require temperature control very precisely in order to prevent leakage or coagulation of material at the nozzle. If you use the hot runner, gate size should be smaller than the cold runner.
4, the chemical and physical properties: PA12 from butadiene linear, semi-crystalline - crystalline thermoplastic material. Its characteristics and PA11 similar, but different crystal structures. The PA12 is a good electrical insulator and polyamide insulation due to moisture will not affect performance. It has good chemical stability, impact resistance machines. PA12 has many of the the plasticizing features and enhancements in terms of improved varieties. Compared to the PA6 and PA66, these materials have a lower melting point and density, with a very high moisture regain. PA12 ability to resist strong oxidizing acids. The viscosity of PA12 depends on the humidity, temperature and storage time. Its good liquidity. Shrinkage of between 0.5% to 2%, which is mainly dependent on the variety of materials, wall thickness, and other process conditions.

PA12	WITCOM		10C-S
PA12	WITCOM		2010/039

Key Words：2010/039，PA12 2010/039，WITCOM 2010/039