PA612 RTP 285 D TFE 13 SI 2Use performance

The performance of the amide plastic
(1) the general performance
PA in the appearance of a transparent or opaque, milky white or yellowish pellets apparent horny, hard, glossy article surface. PA the water absorption is relatively large, the greater the proportion of the amide group, the higher the water absorption, and specifically: of PA6> PA66> PA610 of PA1010 PA11 PA12> PA1212. PA is a self-extinguishing plastic, burning burnt wool or nails taste. PA is a middle barrier plastic, and the increased proportion of the barrier with the amide group / methylene increase, the best effect of the barrier of PA6.
The PA6 with O2 permeability in the order of 25 to 40 cm 3 • mm / m • d • Mpa
CO2 permeability of 150 to 200 cm 3 • mm / m • d • Mpa
The H2O permeability 150g • mm / m • d • Mpa
(2) Mechanical Properties
PA in the room temperature tensile strength and impact strength are high, but the impact strength is not as good as the PC and POM height. With the elevated temperature and humidity of the tensile strength is sharply decreased, while the impact strength is significantly improved. The strength of the glass fiber reinforced PA subject to the influence of temperature and humidity is smaller.
Better fatigue resistance of PA, second only to the POM, fiberglass enhancement processing can also be increased by about 50%.
Poor creep resistance of PA, and suitable for the manufacture of precision the force article can be improved, but the glass fiber reinforced.
PA in abrasion resistance and excellent wear resistance, the wear resistance is a common plastic varieties. The different varieties friction factor is little difference between the non-oil lubrication friction factor of only 0.1 to 0.3. Wear resistance to PA1010. The PA added such as molybdenum disulfide, graphite, F4 and PE friction resistance and abrasion resistance can be further improved.
(3) Thermal Properties
PA's thermal deformation temperature is not high, usually in the 50 to 75 ° C. Glass fiber reinforced more than four-fold increase up to 200 ℃ PA thermal conductivity is very small, only 0.16 to 0.4W / M • K. PA's linear expansion coefficient is large, and to decrease with increasing degree of crystallinity.
(4) Electrical Properties
PA under the conditions of low temperature and low humidity as an excellent insulating material, but the insulation performance with the increase of temperature and humidity and the dramatic deterioration, and is most sensitive to the large proportion of amide group-containing molecule, for example, PA6 greatest PA12 minimum.
(5) environmental performance
PA resistance, chemical stability is excellent, can be resistant to most organic solvents such as alcohols, aromatic hydrocarbons, esters and ketones, etc., especially outstanding oil resistance. PA acid, alkali, salt is bad, can lead to swelling of the most harmful inorganic salts of zinc chloride. PA can be dissolved in formic acid and phenolic compounds.
The poor PA lightfastness strength drops quickly and become brittle in the sun, and therefore can not be used outdoors.

PA612	RTP		285 D
PA612	RTP		285 D SI 2
PA612	RTP		285 D TFE 13 SI 2
PA612	RTP		285 D TFE 15
PA612	RTP		285D TFE 10
PA612	RTP		285D TFE 15 SI 2

Key Words：285 D TFE 13 SI 2，PA612 285 D TFE 13 SI 2，RTP 285 D TFE 13 SI 2